Germanium-on-SOI Infrared Detectors for Integrated Photonic Applications

An overview of recent results on high-speed Ge-on-silicon-on-insulator (Ge-on-SOI) photodetectors and their prospects for integrated optical interconnect applications are presented. The optical properties of Ge and SiGe alloys are described and a review of previous research on Si-on-insulator (SOI) and SiGe detectors is provided as a motivation for the Ge-on-SOI detector approach. The photodetector design is described, which consists of lateral alternating p- and n-type surface contacts on an epitaxial Ge absorbing layer grown on an ultra-thin-SOI substrate. When operated at a bias voltage of -0.5 V, 10 x 10 μm2 devices have dark current, Idark, of only ~ 10 nA, a value that is nearly independent of finger spacing, S, down to S = 0.3 μm. Detectors with S = 1.3 μm have external quantum efficiencies, η, of 52% (38%) at λ = 895 nm (850 nm) with corresponding responsivities of 0.38 A/W (0.26 A/W). The wavelength-dependence of η agrees fairly well with expectations, except at longer wavelengths, where Si up-diffusion into the Ge absorbing layer reduces the efficiency. Detectors with 10 x 10 μm2 area and S = 0.6 μm have -3 dB bandwidths as high as 29 GHz, and can simultaneously achieve a bandwidth of 27 GHz, with Idark = 24 nA, at a bias of only -1 V, while maintaining high efficiency of η = 46% (33%), at λ = 895 nm (850 nm). Analysis of the finger-spacing and area dependence of the device speed indicates that the performance at large finger spacing is transit-time limited, while at small finger spacing, RC delays limit the bandwidth. Methods to improve the device performance are presented, and it is shown that significant improvement in the speed and efficiency both at λ = 850 nm and 1300 nm can be expected by optimizing the layer structure design.

By: S. J. Koester; J. D. Schaub; G. Dehlinger; J. O. Chu

Published in: RC23957 in 2006


This Research Report is available. This report has been submitted for publication outside of IBM and will probably be copyrighted if accepted for publication. It has been issued as a Research Report for early dissemination of its contents. In view of the transfer of copyright to the outside publisher, its distribution outside of IBM prior to publication should be limited to peer communications and specific requests. After outside publication, requests should be filled only by reprints or legally obtained copies of the article (e.g., payment of royalties). I have read and understand this notice and am a member of the scientific community outside or inside of IBM seeking a single copy only.


Questions about this service can be mailed to .